Grade C10C
Corresponding Standard ISO 4954-1-2024
Steels for Cold Heading and Cold Extruding - Technical Delivery Conditions - Part1: Non-Alloy and Alloy Steels
Classification Carbon Steel
C10C Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Cu Mo Al ① More
Minimum Value 0.08 - 0.3 - - - - - - 0.02 Cr+Ni+Mo≤0.50
Maximum Value 0.12 0.1 0.5 0.025 0.025 0.3 0.3 0.3 0.1 0.06
C10C Mechanical Properties
diameter
d
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
5＜d≤100 +AR or
+AR+PE		 ≤430 ≥60*
5＜d≤100 +AC or
+AC+PE		 ≤380 ≥70
5＜d≤10 +AR+C ≤520 ≥58
10＜d≤40 ≤510 ≥58
2≤d≤5 +AR+C+AC ≤370 ≥72
5＜d≤10 ≤360 ≥72
10＜d≤40 ≤360 ≥72
2≤d≤5 +AR+C+AC+LC ≤410 ≥68
5＜d≤40 ≤400 ≥68
5＜d≤10 +AC+C ≤470 ≥63
10＜d≤40 ≤460 ≥63
①+AR=as hot-rolled；+AR or +PE=as hot-rolled or peeled；+AR+C=as hot-rolled+cold drawn；+AR+C+AC=as hot-rolled+cold drawn+spheroidized；+AR+C+AC+LC=as hot-rolled+cold drawn+spheroidized+skin passed；+AC= spheroidized ；+AC or +AC+PE=spheroidized or spheroidized+peeled；+AC+C=spheroidized +cold drawn；+FP=treated to ferrite-pearlite structure and hardness range；+AC+C+AC=spheroidized +cold drawn + spheroidized；+AC+C+AC+LC=spheroidized +cold drawn + spheroidized + skin passed
• Mechanical properties of wire rod, bars and wire not intended for heat treatment after cold working
* The values are given only for information.
1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
Japan International Organization for Standardization European Standard
JIS ISO EN Numerical Grade
SWRCH10A C10C C10C 1.0214
2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM ISO EN Numerical Grade
ML10Al U40108 SWRCH10A 1010 CC11A
C10C 		C10C 1.0214
C10C Corresponding Standards(Same grade name, different standards)
1 EN 10263-2-2001
C10C 1.0214
2 Q/BQB 517-2018
C10C
3 DIN EN 10263-2-2017
C10C 1.0214
4 EN 10263-2-2017
C10C 1.0214
5 ISO 4954-2018
C10C
6 ISO 4954-1-2024
C10C

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!