022Cr19Ni13Mo3 S31703 00Cr19Ni13Mo3 317L - GB /T 1220-2007

Grade	022Cr19Ni13Mo3
China ISC	S31703
Other Names
Old Grade
Corresponding Standard	GB /T 1220-2007 Stainless Steel Bars
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance

022Cr19Ni13Mo3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	-	-	-	-	-	18	11	3
Maximum Value	0.03	1	2	0.045	0.03	20	15	4

022Cr19Ni13Mo3 Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
d≤180	Solid Solution Treatment	≥480	≥175	≥40	≥60	HBW:≤217 HRB:≤95 HV:≤220

• This does not apply to flat bars, but if required by the buyer, it shall be determined through negotiation between the supplier and the buyer.

Approximate Comparison Table Austenitic Stainless Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

022Cr19Ni13Mo3
(00Cr19Ni13Mo3)

S31703

317L

SUS 317L

STS 317L

317L

S31703

X2CrNiMo 19-14-4
X2CrNiMo18-15-4

X2CrNiMo 18-15-4
(X2CrNiMo 18-16)

1.4438

Z2CND 19-15
Z3CND 19-15-04

X2CrNiMo 18-15-4

1.4438

03Х16Н15М3

2367

317S12
317S11

022Cr19Ni13Mo3 Corresponding Standards(Same grade name, different standards)

1	GB /T 20878-2007
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)
2	GB /T 1220-2007
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3) 317L
3	GB /T 4356-2016
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)
4	GB /T 3280-2015
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)
5	GB /T 4237-2015
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)
6	GB /T 14975-2012
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)
7	GB /T 14976-2012
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)
8	GB /T 24511-2017
	022Cr19Ni13Mo3 S31703
9	GB /T 32569-2016
	022Cr19Ni13Mo3 S31703
10	GB /T 20878-2024
	022Cr19Ni13Mo3 S31703 (00Cr19Ni13Mo3)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!