ML37Cr A20374 - GB T 6478-2001

Grade	ML37Cr
China ISC	A20374
Corresponding Standard	GB T 6478-2001 Steels for cold heading and cold extruding
Classification	Alloy Steel

ML37Cr Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni ^*	Cu ^*
Minimum Value	0.34	-	0.6	-	-	0.9	-	-
Maximum Value	0.41	0.3	0.9	0.035	0.035	1.2	0.2	0.2

①By agreement between the supplier and the purchaser, other grades of cold heading and cold extrusion steel may be supplied.
②Permissible deviations in the chemical composition of the steel shall comply with the relevant provisions of GB/T 222-1984.

ML37Cr Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %
Steel	Annealing	≤600			≥60
Sample diameter d=25	Normalizing temperature 850~880°C, Quenching temperature 830~870°C water or oil cooling, Tempering temperature 540~680°C	≥850	≥630	≥14

New and Old Grade Replacement List

Corresponding Standard	Grade
GB T 6478-2001	Grade China ISC
GB /T 6478-2015	Grade China ISC Old Grade

Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		International Organization for Standardization
GB	ISC	ISO
ML37CrB GB/T 6478-2015	A20374	37CrB1E ISO 4954-1993

ML37Cr Corresponding Standards(Same grade name, different standards)

1	GB T 6478-2001
	ML37Cr A20374
2	GB /T 6478-2015
	(ML37Cr) ML35Cr A20354