1Cr17 S11710 - GB /T 12770-2002

Grade	1Cr17
China ISC	S11710
Corresponding Standard	GB /T 12770-2002 Welded Stainless Steel Tubes for Machine Structures
Classification	Ferritic Stainless Steel

1Cr17 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni
Minimum Value	-	-	-	-	-	16	-
Maximum Value	0.12	0.75	1	0.035	0.03	18	0.6

1Cr17 Mechanical Properties

Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %
A	≥410	≥210	≥20

1 Approximate Comparison Table Ferritic Stainless Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

Numerical Grade

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

10Cr17
(1Cr17)

S11710

430

SUS 430

STS 430

430

S43000

X6Cr 17
8
ISO 683-13-1986

4016-430-00-I

X6Cr 17
(X8Cr 17)

1.4016

Z8C 17

X6Cr 17

1.4016

12Х 17

2320

430S15

2 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding

China		Japan	United States		International Organization for Standardization		European Standard
GB	ISC	JIS	ASTM/AISI	UNS	ISO	Numerical Grade	EN	Numerical Grade
10Cr17 (1Cr17)	S11710	SUS430	430	S43000	X6Cr17	4016-430-00-I	X6Cr17	1.4016

1Cr17 Corresponding Standards(Same grade name, different standards)

1	GB /T 20878-2007
	(1Cr17) 10Cr17 S11710
2	GB /T 1221-2007
	(1Cr17) 10Cr17 S11710
3	GB /T 1220-2007
	(1Cr17) 10Cr17 S11710
4	GB /T 4240-2019
	(1Cr17) 10Cr17 S11710
5	GB /T 4356-2016
	(1Cr17) 10Cr17 S11710
6	GB /T 3280-2015
	(1Cr17) 10Cr17 S11710
7	GJB 2294-1995
	1Cr17
8	GB /T 4238-2015
	(1Cr17) 10Cr17 S11710
9	GB /T 4237-2015
	(1Cr17) 10Cr17 S11710
10	GB /T 14975-2012
	(1Cr17) 10Cr17 S11710
11	GB /T 14976-2012
	(1Cr17) 10Cr17 S11710
12	JG /T 3030-1995
	1Cr17
13	GJB 2294A-2014
	(1Cr17) 10Cr17
14	GB /T 20878-2024
	(1Cr17) 10Cr17 S11710
15	GB /T 12770-2002
	1Cr17 S11710

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!