06Cr18Ni12Mo2Cu2 S31688 0Cr18Ni12Mo2Cu2 - GB /T 1220-2007

06Cr18Ni12Mo2Cu2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo
Minimum Value	-	-	-	-	-	17	10	1	1.2
Maximum Value	0.08	1	2	0.045	0.03	19	14	2.5	2.75

06Cr18Ni12Mo2Cu2 Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
d≤180	Solid Solution Treatment	≥520	≥205	≥40	≥60	HBW:≤187 HRB:≤90 HV:≤200

• This does not apply to flat bars, but if required by the buyer, it shall be determined through negotiation between the supplier and the buyer.

Approximate Comparison Table Austenitic Stainless Steel

06Cr18Ni12Mo2Cu2 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!