06Cr19Ni13Mo3 S31708 0Cr19Ni13Mo3 - GB /T 1220-2007

06Cr19Ni13Mo3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	-	-	-	-	-	18	11	3
Maximum Value	0.08	1	2	0.045	0.03	20	15	4

06Cr19Ni13Mo3 Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
d≤180	Solid Solution Treatment	≥520	≥205	≥40	≥60	HBW:≤187 HRB:≤90 HV:≤200

• This does not apply to flat bars, but if required by the buyer, it shall be determined through negotiation between the supplier and the buyer.

1 Approximate Comparison Table Austenitic Stainless Steel

2 Approximate Comparison Table Austenitic Heat-Resistant Steel

3 Approximate Comparison Table Austenitic Stainless Steel

China	Japan	United States	International Organization for Standardization		European Standard
ISC	JIS	UNS	ISO	Numerical Grade	Numerical Grade
S31708	SUS317	S31700	X6CrNiMo19-13-4	4445-317-00-U	(1.4445)

06Cr19Ni13Mo3 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!