Y108Cr17 S44097 Y11Cr17 - GB /T 1220-2007

Grade	Y108Cr17
China ISC	S44097
Old Grade
Corresponding Standard	GB /T 1220-2007 Stainless Steel Bars
Classification	Martensitic Stainless Steel

Y108Cr17 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	0.95	-	-	-	0.15	16	-	-
Maximum Value	1.2	1	1.25	0.06	-	18	0.6	0.75

Y108Cr17 Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Steel bars; d≤75	Annealing					≤269
Sample; d≤75	Quenching + Tempering	-	-	-	-	HRC ≥58	-

• This does not apply to flat bars, but if required by the buyer, it shall be determined through negotiation between the supplier and the buyer.

1 Approximate Comparison Table Martensitic Stainless Steel

2 Approximate Comparison Table Martensitic Stainless Steel

China		Japan	International Organization for Standardization		European Standard
GB	ISC	JIS	ISO	Numerical Grade	Numerical Grade
Y108Cr17 (Y11Cr17)	S44097	SUS440F	X110CrS17	4025-440-74-X	(1.4025)

Y108Cr17 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!