32Cr13Mo S45830 3Cr13Mo - GB /T 1220-2007

Grade	32Cr13Mo
China ISC	S45830
Old Grade
Corresponding Standard	GB /T 1220-2007 Stainless Steel Bars
Classification	Martensitic Stainless Steel

32Cr13Mo Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	0.28	-	-	-	-	12	-	0.5
Maximum Value	0.35	0.8	1	0.04	0.03	14	0.6	1

32Cr13Mo Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Steel bars; d≤75	Annealing					≤207
Sample; d≤75	Quenching + Tempering	-	-	-	-	HRC ≥50	-

• This does not apply to flat bars, but if required by the buyer, it shall be determined through negotiation between the supplier and the buyer.

Approximate Comparison Table

China	International Organization for Standardization		European Standard
ISC	ISO	Numerical Grade	Numerical Grade
S45830	X38CrMo14	4419-420-97-E	1.4419

32Cr13Mo Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!