Home Material GB /T 1221-2007
简体 | 繁體
Grade 40Cr10Si2Mo
China ISC S48140
Old Grade
Corresponding Standard GB /T 1221-2007
Heat-resistant Steel Bars
Classification Martensitic Stainless Steel
40Cr10Si2Mo Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Mo
Minimum Value 0.35 1.9 - - - 9 - 0.7
Maximum Value 0.45 2.6 0.7 0.035 0.03 10.5 0.6 0.9
40Cr10Si2Mo Mechanical Properties
diameter
d
mm		 Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
d≤75 Quenching + Tempering
≥885		 Quenching + Tempering
≥685		 Quenching + Tempering
≥10		 Annealing
≤269
1 Approximate Comparison Table
China Taiwan, China Japan South Korea Germany France European Standard Russia
GB ISC CNS JIS KS DIN EN/DIN W-Nr. NF EN/NF EN GOST
40Cr10Si2Mo
(4Cr10Si2Mo) 		S48140 SUH 3 SUH 3 STR 3 X40CrSiMo 10-2 1.4731 Z40CSD 10 X40CrSiMo 10
X40CrSiMo 10-2 		40Х10С2М
2 Approximate Comparison Table
China Taiwan, China Japan South Korea Germany France European Standard Russia
GB ISC CNS JIS KS DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST
40Cr10Si2Mo
(4Cr10Si2Mo) 		S48140 3 SUH 3 STR 3 X40CrSiMo 10-2 1.4731 Z40CSD 10 X40CrSiMo 10 1.4731 40Х10С2М
40Cr10Si2Mo Corresponding Standards(Same grade name, different standards)
1 GB /T 20878-2007
40Cr10Si2Mo S48140 (4Cr10Si2Mo)
2 GB /T 1221-2007
40Cr10Si2Mo S48140 (4Cr10Si2Mo)
3 GJB 2294A-2014
40Cr10Si2Mo (4Cr10Si2Mo)
4 GB /T 12773-2021
40Cr10Si2Mo

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!