Home Material EN 485-2-2016(+A1:2018)
简体 | 繁體
Grade EN AW-Al Si1MgMn
European Standard Steel Grade EN AW-6082
Corresponding Standard EN 485-2-2016(+A1:2018)
Aluminium and Aluminium Alloys - Sheet, Strip and Plate
Classification Aluminum and Aluminum Alloys
EN AW-Al Si1MgMn Chemical Element Composition Content (%)
Component Fe Si Mn Cr Cu Ti Zn Mg Other Individual Other Total More
Minimum Value - 0.7 0.4 - - - - 0.6 - - Al:Rem
Maximum Value 0.5 1.3 1 0.25 0.1 0.1 0.2 1.2 0.05 0.15
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
◎Chemical composition in accordance with EN 573-3-2019+A2-2023
EN AW-Al Si1MgMn Mechanical Properties
thickness
t
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Specified Plastic Yield Strength
Rp0.2
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
0.4≤t≤1.5 Annealing (O) ≤150 ≤85 A50mm
≥14		 40
1.5＜t≤3 ≤150 ≤85 ≥16 40
3＜t≤6 ≤150 ≤85 ≥18 40
6＜t≤12.5 ≤150 ≤85 ≥17 40
12.5＜t≤25 ≤155 A
≥16		 40
0.4≤t≤1.5 T4，T451 ≥205 ≥110 A50mm
≥12		 58
1.5＜t≤3 ≥205 ≥110 ≥14 58
3＜t≤6 ≥205 ≥110 ≥15 58
6＜t≤12.5 ≥205 ≥110 ≥14 58
12.5＜t≤40 ≥205 ≥110 A
≥13		 58
40＜t≤80 ≥205 ≥110 ≥12 58
0.4≤t≤1.5 T42 ≥205 ≥95 A50mm
≥12		 57
1.5＜t≤3 ≥205 ≥95 ≥14 57
3＜t≤6 ≥205 ≥95 ≥15 57
6＜t≤12.5 ≥205 ≥95 ≥14 57
12.5＜t≤40 ≥205 ≥95 A
≥13		 57
40＜t≤80 ≥205 ≥95 ≥12 57
0.4≤t≤1.5 T6，T651，T62 ≥310 ≥260 A50mm
≥6		 94
1.5＜t≤3 ≥310 ≥260 ≥7 94
3＜t≤6 ≥310 ≥260 ≥10 94
6＜t≤12.5 ≥300 ≥255 ≥9 91
12.5＜t≤60 ≥295 ≥240 A
≥8		 89
60＜t≤100 ≥295 ≥240 ≥7 89
100＜t≤150 ≥275 ≥240 ≥6 84
150＜t≤175 ≥275 ≥230 ≥4 83
175＜t≤350 ≥260 ≥220 ≥2
0.4≤t≤1.5 T61，T6151 ≥280 ≥205 A50mm
≥10		 82
1.5＜t≤3 ≥280 ≥205 ≥11 82
3＜t≤6 ≥280 ≥205 ≥11 82
6＜t≤12.5 ≥280 ≥205 ≥12 82
12.5＜t≤60 ≥275 ≥200 A
≥12		 81
60＜t≤100 ≥275 ≥200 ≥10 81
100＜t≤150 ≥275 ≥200 ≥9 81
150＜t≤170 ≥275 ≥200 ≥8 81
◎The hardness is for reference only
◎T4：Solution heat-treated 4 and naturally aged to a substantially stable condition；T42: solution heat-treated from annealed or F temper and naturally aged to a substantially stable condition;
◎T6: Solution heat treated 4 and then artificially aged；T62：solution heat-treated from annealed or F temper and artificially aged;
◎T61: solution heat-treated and then artificially aged in underageing conditions to improve formability
◎T451、T651：Stretched the indicated amounts after solution heat-treatment or after cooling from an elevated temperature shaping process，For example, plates: 1.5 to 3% permanent set (deformation)
◎T6151: solution heat-treated, stress-relieved by stretching a controlled amount (permanent set 0,5 % to 3 % for sheet, 1,5 % to 3 % for plate) and then artificially aged in underageing conditions to improve formability. The products receive no further straightening after stretching。
ENAW-AlSi1MgMn Corresponding Standards(Same grade name, different standards)
1 EN 573-3-2003
EN AW-Al Si1MgMn EN AW-6082
2 EN 485-2-2016(+A1:2018)
EN AW-Al Si1MgMn EN AW-6082
3 EN 13195-2013
EN AW-Al Si1MgMn EN AW-6082

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!