C10C 1.0214 - DIN EN 10263-2-2002

Grade	C10C
Germany W-Nr.	1.0214
Corresponding Standard	DIN EN 10263-2-2002 Steel Rod,bars and Wire for Cold Heading and Cold Extrusion - Part 2: Technical Delivery Conditions for Steels Not Intended for Heat Treatment after Cold Working
Classification	Carbon Steel

C10C Chemical Element Composition Content (%)

Component	C	Si ^①	Mn	P	S	Al ^②
Minimum Value	0.08	-	0.3	-	-	0.02
Maximum Value	0.12	0.1	0.5	0.025	0.025	0.06

C10C Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
5＜d≤100	+U or +U+PE	≤430	≥60
5＜d≤100	+AC or +AC+PE	≤380	≥70
5＜d≤10	+U+C	≤520	≥58
10＜d≤40	+U+C	≤510	≥58
2＜d≤5	+U+C+AC	≤370	≥72
5＜d≤40	+U+C+AC	≤360	≥72
2＜d≤5	+U+C+AC+LC	≤410	≥68
5＜d≤40	+U+C+AC+LC	≤400	≥68
5＜d≤10	+AC+C	≤470	≥63
10＜d≤40	+AC+C	≤460	≥63

New and Old Grade Replacement List

Approximate Comparison Table Cold Heading Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML10

U40102

SWRCH10K

1012

G10120

CC8A
(A2Al)

QSt36-3
(C11C)

1.0214

XC10
FB10
FR10

10кл

0/2

C10C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!