C8C 1.0213 - DIN EN 10263-2-2002

Grade	C8C
Germany W-Nr.	1.0213
Corresponding Standard	DIN EN 10263-2-2002 Steel Rod,bars and Wire for Cold Heading and Cold Extrusion - Part 2: Technical Delivery Conditions for Steels Not Intended for Heat Treatment after Cold Working
Classification	Carbon Steel

C8C Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Al ^*
Minimum Value	0.06	-	0.25	-	-	0.02
Maximum Value	0.1	0.1	0.45	0.02	0.025	0.06

C8C Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
5＜d≤100	+U or +U+PE	≤410	≥65
5＜d≤100	+AC or AC+PE	≤360	≥70
5＜d≤10	+U+C	≤490	≥63
10＜d≤40	+U+C	≥480	≥63
2＜d≤5	+U+C+AC	≤350	≥72
5＜d≤40	+U+C+AC	≤340	≥72
2＜d≤5	+U+C+AC+LC	≤390	≥68
5＜d≤40	+U+C+AC+LC	≤380	≥68
5＜d≤10	+AC+C	≤450	≥65
10＜d≤40	+AC+C	≤440	≥65

New and Old Grade Replacement List

Approximate Comparison Table Cold Heading Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML08Al

U40088

SWRCH8A

1010

G10100

CC8X
(A2R)

QSt34-3
(C7C)

1.0213

FB8
FR8

08Ю

0/1

C8C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!