C1100 C1100T C1100TS - JIS H 3300-2018(勘误2019)

Grade	C1100
Other Names
Corresponding Standard	JIS H 3300-2018(勘误2019) Copper and Copper Alloy Seamless Pipes and Tubes
Classification	Copper and Copper Alloys

C1100 Chemical Element Composition Content (%)

Component	Cu
Minimum Value	99.9
Maximum Value	-

C1100 Mechanical Properties

out diameter, wall thickness d,t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Hardness HBW
5≤d≤250, 0.5≤t≤30	C1100T-O C1100TS-O	O	≥205	≥40
5≤d≤250, 0.5≤t≤25	C1100T-1/2H C1100TS-1/2H	1/2H	245~325		HV 70~110
5≤d≤100, 0.5≤t≤6	C1100T-H C1100TS-H	H	≥275		HV ≥88
5≤d≤100, 6＜t≤10	C1100T-H C1100TS-H	H	≥265		HV ≥83

1 Approximate Comparison Table Processing Pure Copper, Silver Copper

China		Japan	United States		International Organization for Standardization		Germany		France	European Standard	Russia
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	NF EN/NF	EN	GOST
T2	T11050	C1100 Cu99.90	99.90Cu	C11000	Cu-FRHC	C11000	ECu-57	C11000 2.0090	Cu-FRHC C11000	Cu-FRHC	М1

2 Approximate Comparison Table Copper and Copper Alloy

Japan	United States	International Organization for Standardization	Germany		France	European Standard		Russia	Sweden	United Kingdom
JIS	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
C1100	C11000	Cu-ETP	E-Cu58 E2-Cu58	2.0065	CuA1	Cu-ETP	CW004A	M1	5010	C101

3 Approximate Comparison Table Processing Pure Copper, Silver Copper

China	Japan	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	BS EN/BS
T2	C1100	C11000	Cu-FRHC	E-Cu58	C101 C102

C1100 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!