C2800 C2800T C2800TS - JIS H 3300-2018(勘误2019)

Grade	C2800
Other Names
Corresponding Standard	JIS H 3300-2018(勘误2019) Copper and Copper Alloy Seamless Pipes and Tubes
Classification	Copper and Copper Alloys

C2800 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	More
Minimum Value	-	59	-	Zn:Rem
Maximum Value	0.07	63	0.1	Zn:Rem

C2800 Mechanical Properties

out diameter, wall thickness d,t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Hardness HBW
10≤d≤250, 1≤t≤15	C2800T-O C2800TS-O	O	≥315	≥125	≥35
10≤d≤250, 1≤t≤15	C2800T-OL C2800TS-OL	OL	≥315		≥35	HRFS ≤90
10≤d≤250, 1≤t≤6	C2800T-1/2H C2800TS-1/2H	1/2H	≥375		≥15	HR30TS ≥55
10≤d≤100, 1≤t≤6	C2800T-H C2800TS-H	H	≥450

1 Approximate Comparison Table Brass

China		Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
H59	T28200	C2800	60Cu-40Zn	C28000	CuZn40	C28000	CuZn40	C28000 2.0360	CuZn40	CW509L	Л60 L60

2 Approximate Comparison Table Brass

3 Approximate Comparison Table Brass

China	Japan	United States	International Organization for Standardization	United Kingdom
GB	JIS	ASTM	ISO	BS EN/BS
H62	C2800	C28000	CuZn40	CZ109

C2800 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!