N05500 Monel K500 - SAE J 470c-1976

Commercial Grade
USA UNS	N05500
Other Names
Corresponding Standard	SAE J 470c-1976 Wrought Nickel and Nickel - Related Alloys
Brand/Supplier	America ->
Classification	Special Alloy Steel
Properties	Strength Hardness Corrosion Resistance Machinability
Density	8.47 g/cm³

Chemical Element Composition Content (%)

	Component	Fe	C	Si	Mn	S	Ni	Cu	Ti	Al
Standard	Minimum Value	-	-	-	-	-	-	-	-	-
	Maximum Value	-	-	-	-	-	-	-	-	-
	Nominal Value	1	0.15	0.25	0.75	0.005	66	29	0.6	2.75

	Component	Fe	C	Si	Mn	S	Ni ^*	Cu	Ti	Al
SMC	Minimum Value	-	-	-	-	-	63	27	0.35	2.3
	Maximum Value	2	0.25	0.5	1.5	0.01	-	33	0.85	3.15
	Nominal Value	-	-	-	-	-	-	-	-	-

Standard - refers to the chemical composition specified in this standard
SMC- refers to the chemical composition of this grade of product produced by Speical metals corporation
*Include Co

Mechanical Properties

Products Form	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Bars, Forgings, Wire, Thin sheet, Strip, Tubes	Standard		620~1380	276~1207	2~45	25~70	110~250	203~298
Rod	SMC	Hot-Finished	621~1069	276~758	20~45	-	140~315	-
Rod	SMC	Hot-Finished, Aged	965~1310	690~1034	20~30	-	265~346	-
Rod	SMC	Hot-Finished, Annealed	621~758	276~414	25~45	-	140~185	-
Rod	SMC	Hot-Finished, Annealed and Aged	896~1138	586~827	20~35	-	250~315	-
Rod	SMC	Cold-Drawn, As-Drawn	690~965	483~862	13~35	-	175~260	-
Rod	SMC	Cold-Drawn, Aged	931~1276	655~1103	15~30	-	255~370	-
Rod	SMC	Cold-Drawn, Annealed	621~758	276~414	25~50	-	140~185	-
Rod	SMC	Cold-Drawn, Annealed and Aged	896~1310	586~827	20~30	-	250~315	-
Cold rolled thin plate	SMC	Annealing	621~724	276~448	25~45	-	HRB ≤85	-
Cold-rolled strip	SMC	Annealing	621~724	276~448	25~45	-	HRB ≤85	-
Cold-rolled strip	SMC	Annealing and aging	896~1172	621~827	15~25	-	HRC ≥24	-
Cold-rolled strip	SMC	Spring Temper	1000~1138	896~1103	3~8	-	HRC ≥25	-
Cold-rolled strip	SMC	Spring Temper, Aged	1172~1517	896~1345	5~10	-	HRC ≥34	-
Seamless Pipe	SMC	Cold-Drawn, Annealed	621~758	276~448	25~45	-	HRB ≤90	-
Seamless Pipe	SMC	Cold-Drawn, Annealed and Aged	896~1241	586~827	15~30	-	HRC 24~36	-
Seamless Pipe	SMC	Cold-Drawn, As-Drawn	758~1103	586~965	2~15	-	HR95B~32C	-
Seamless Pipe	SMC	Cold-Drawn, As-Drawn, Aged	965~1517	690~1379	3~25	-	HRC 27~40	-
Plate	SMC	Hot-Finished	621~931	276~758	20~45	-	HR75B~26C	-
Plate	SMC	Hot-Finished, Aged	965~1241	690~981	20~30	-	HRC 27~37	-
Cold drawn wire	SMC	Annealing	552~758	241~448	20~40	-	-	-
Cold drawn wire	SMC	Annealing and aging	827~1034	621~758	15~30	-	-	-
Cold drawn wire	SMC	Spring Temper	1000~1310	896~1241	2~5	-	-	-
Cold drawn wire	SMC	Spring Temper, Aged	1103~1379	965~1310	3~8	-	-	-

Approximate Comparison Table Corrosion-Resistant Alloy

China		United States		Germany
GB	ISC	Commercial Grade	UNS	W-Nr.
NS 6500 Ni68Cu28Al	H 05500	Monel K500	N 05500	2.4375