X6CrNi 18-10 1.4948 - EN 10088-1-2005

Grade	X6CrNi 18-10
European Standard Steel Grade	1.4948
Corresponding Standard	EN 10088-1-2005 Staehle Stainless steels. Part 1:List of stainless steels
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance
Density	7.9 g/cm³

X6CrNi 18-10 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	N
Minimum Value	0.04	-	-	-	-	17	8	-
Maximum Value	0.08	1	2	0.035	0.015	19	11	0.11

① Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

1 Approximate Comparison Table Austenitic Stainless Steel

China		Japan	United States		International Organization for Standardization	Germany		European Standard
GB	ISC	JIS	AISI	UNS	ISO	DIN EN/DIN	W-Nr.	EN	Numerical Grade
07Cr19Ni10	S30409	SUS 304H	304H	S30409	X6CrNi 18-10 X7CrNi 18-9	X6CrNi18-10	1.4948	X6CrNi18-10	1.4948

2 Approximate Comparison Table

Japan	United States		International Organization for Standardization	France	European Standard		Russia
JIS	ASTM	UNS	ISO	NF EN/NF	EN	Numerical Grade	GOST
SUS304H	304H	S30409	X7CrNi18-9	Z6CN18-09	X6CrNi18-10	1.4948	08KH18N10

3 Approximate Comparison Table Seamless Steel Tubes and Pipes for High Pressure Boiler

China		United States	European Standard
GB	ISC	ASTM/AISI	EN
10Cr9MoW2VNbBN	S30409	SA-213 TP304H	X6CrNi18-10

X6CrNi18-10 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X6CrNi 18-10 1.4948
2	EN 10269-2006
	X6CrNi18-10 1.4948
3	EN 10269-2013
	X6CrNi 18-10 1.4948
4	NF EN 10269-1999
	X6CrNi18-10 1.4948
5	DIN EN 10269-2014
	X6CrNi 18-10 1.4948
6	ISO 9328-7-2018
	X6CrNi18-10
7	EU 95-1979
	X6CrNi 18-10
8	NF EN 10088-1-2005
	X6CrNi18-10 1.4948
9	NF EN 10028-7-2008
	X6CrNi18-10 1.4948
10	NF EN 10028-7-2000
	X6CrNi18-10 1.4948

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!