10Cr17 S11710 1Cr17 - GB /T 3280-2015

Grade	10Cr17
China ISC	S11710
Old Grade
Corresponding Standard	GB /T 3280-2015 Cold rolled stainless steel plate and strip
Classification	Ferritic Stainless Steel
Properties	Corrosion Resistance
Density	7.7 g/cm³

10Cr17 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni
Minimum Value	-	-	-	-	-	16	-
Maximum Value	0.12	1	1	0.04	0.03	18	0.75

10Cr17 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Steel plates, steel strips	Annealing	≥420	≥205	≥22	≤183

1 Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

Numerical Grade

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

10Cr17
(1Cr17)

S11710

430

SUS 430

STS 430

430

S43000

X6Cr 17
8
ISO 683-13-1986

4016-430-00-I

X6Cr 17
(X8Cr 17)

1.4016

Z8C 17

X6Cr 17

1.4016

12Х 17

2320

430S15

2 Approximate Comparison Table Stainless steels for cold heading and cold extruding

China		Japan	United States		International Organization for Standardization		European Standard
GB	ISC	JIS	ASTM/AISI	UNS	ISO	Numerical Grade	EN	Numerical Grade
10Cr17 (1Cr17)	S11710	SUS430	430	S43000	X6Cr17	4016-430-00-I	X6Cr17	1.4016

10Cr17 Corresponding Standards(Same grade name, different standards)

1	GB /T 20878-2007
	10Cr17 S11710 (1Cr17)
2	GB /T 1221-2007
	10Cr17 S11710 (1Cr17)
3	GB /T 1220-2007
	10Cr17 S11710 (1Cr17)
4	GB /T 4240-2019
	10Cr17 S11710 (1Cr17)
5	GB /T 4356-2016
	10Cr17 S11710 (1Cr17)
6	GB /T 3280-2015
	10Cr17 S11710 (1Cr17)
7	GB /T 4238-2015
	10Cr17 S11710 (1Cr17)
8	GB /T 4237-2015
	10Cr17 S11710 (1Cr17)
9	GB /T 14975-2012
	10Cr17 S11710 (1Cr17)
10	GB /T 14976-2012
	10Cr17 S11710 (1Cr17)
11	GJB 2294A-2014
	10Cr17 (1Cr17)
12	GB /T 20878-2024
	10Cr17 S11710 (1Cr17)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!