Grade 06Cr25Ni20
China ISC S31008
Old Grade
Corresponding Standard GB /T 4237-2015
Hot rolled stainless steel plate,sheet and strip
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
06Cr25Ni20 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni
Minimum Value - - - - - 24 19
Maximum Value 0.08 1.5 2 0.045 0.03 26 22
06Cr25Ni20 Mechanical Properties
Heat Treatment or Condition
Tensile Strength
σb
Mpa
Specified Plastic Yield Strength
Rp0.2
Mpa
Elongation or Extension Rate
δ
%
Reduction of Area
ψ
%
solution ≥515 ≥205 ≥40 HBW:≤217
HRB:≤95
HV:≤220
②A50mm sample is used when the thickness is less than 3mm
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr25Ni20
(0Cr25Ni20)
S31008 310S SUS 310S STS 310S 310S S31008 ~X12CrNi 23-13
X6CrNi25-20
X12CrNi 25-21 1.4845 Z12CN 25-20 X12CrNi 23-12
X6CrNi25-20
1.4845
1.4951
10Х23Н18 2361 304S24
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr25Ni20
(0Cr25Ni20)
1Cr25Ni20Si2
S31008 310S SUS 310S STS 310S 310S S31008 X8CrNi 25-21 X12CrNi 25-21
X8CrNi 25-21
1.4845
1.4845
Z12CN 25-20 X8CrNi 25-21 1.4845 ~08Х23Н18 2361 304S24

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!