Commercial Grade
USA UNS N06601
Other Names
Corresponding Standard SAE J 470c-1976
WROUGHT NICKEL AND NICKEL-RELATED ALLOYS
Brand/Supplier
America ->
Classification Nickel and Nickel Alloys
Properties Corrosion Resistance Weldability
Density 8.11 g/cm3
Chemical Element Composition Content (%)
  Component Fe C Si Mn Cr Ni Cu Al More
Standard Minimum Value - - - - - - - - Fe:Remainder
Maximum Value - - - - - - - -
Nominal Value 13 0.1 0.5 1 23 60.5 1 1.3
  Component C Si Mn S Cr Ni Cu Al More
SMC Minimum Value - - - - 21 58 - 1 Fe:Remainder
Maximum Value 0.1 0.5 1 0.015 25 63 1 1.7
Nominal Value - - - - - - - -
Standard - This standard element content is an average or nominal value. For more precise content values, contact the manufacturer.
Chemical composition data of SMC-Special metals corporation
Mechanical Properties
condition Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
Rod SMC Hot-Finished 585~825 240~690 15~60 Rb
65~95
Rod SMC Annealing 550~790 205~415 40~70 Rb
60~80
Plate SMC Annealing 550~690 205~310 45~65 Rb
60~75
Thin plate SMC Cold-Rolled 790~1310 690~1205 2~20 -
Thin plate SMC Annealing 585~690 205~345 35~55 Rb
65~80
Strip SMC Cold-Rolled 790~1310 690~1205 2~20 -
Strip SMC Annealing 585~690 205~345 35~55 Rb
65~80
Tube SMC Annealing 550~760 205~415 35~65 Rb
70~95
Wire SMC Cold-Drawn 825~1415 690~1345 3~20 -
Wire SMC Annealing 620~790 240~480 35~45 -
All Forms SMC Solution Heat Treatment 515~760 160~380 40~75 Rb
55~95
1 Approximate Comparison Table corrosion-resistant alloy
China Japan South Korea United States Germany
GB ISC JIS KS Commercial Grade UNS W-Nr. L-Nr.
NS 3103
(NS 313)
(1Cr23Ni60Fe13Al) 		H 06601
H 03103 		NCF 601 NCF 601 Inconel 601 N 06601 NiCr23Fe 2.4851
2 Approximate Comparison Table
China United States International Organization for Standardization
GB ISC ASTM AWS ISO
HNS 3103
NiCr23Fe15Al 		W 56601 N 06601 ERNiCrFe-11 SNi 6601