C2800 C2800 BE C2800 BD - JIS H 3250-2015

Grade	C2800
Other Names
Corresponding Standard	JIS H 3250-2015 Copper and copper alloy rods and bars
Classification	Copper and Copper Alloys

C2800 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	More
Minimum Value	-	59	-	Zn:余量
Maximum Value	0.07	63	0.1	Zn:余量

C2800 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %
Extruded bars (BE); d ≥ 6	As fabricated(F)	≥315	≥25
Drawn bars (BD); 2 ≤ d < 6	Annealing (O)	≥315	≥20
Drawn bars (BD); 6 ≤ d ≤ 75	Annealing (O)	≥315	≥35
Drawn bars (BD); 2 ≤ d ≤ 6	1/2 Hard (1/2H)	≥375	≥10
Drawn bars (BD); 6 ≤ d ≤ 50	1/2 Hard (1/2H)	≥375	≥15
Drawn bars (BD); 2 ≤ d ≤ 20	Hard (H)	≥450

1 Approximate Comparison Table Brass

China		Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
H59	T28200	C2800	60Cu-40Zn	C28000	CuZn40	C28000	CuZn40	C28000 2.0360	CuZn40	CW509L	Л60

2 Approximate Comparison Table Brass

3 Approximate Comparison Table Brass

China	Japan	United States	International Organization for Standardization	United Kingdom
GB	JIS	ASTM	ISO	BS EN/BS
H62	C2800	C28000	CuZn40	CZ109

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!