Home Material DIN 1654-3-1989
简体 | 繁體
Grade 17Cr 3
Germany W-Nr. 1.7016
Old Grade
Corresponding Standard DIN 1654-3-1989
Classification Alloy Steel
Properties Forgability
17Cr 3 Chemical Element Composition Content (%)
Component C Si Mn P S Cr
Minimum Value 0.14 - 0.4 - - 0.6
Maximum Value 0.2 0.4 0.7 0.035 0.035 0.9
• The chemical composition of the steel is consistent with that specified in DIN 17210-1986.
17Cr 3 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Hot-rolled bars, wire rods Spheroidizing Annealing (GKZ) or Spheroidizing Annealing (GKZ) + Pickling (SH) ≤520 ≥60
Drawn products Cold Drawing (K) + Spheroidizing Annealing (GKZ) ≤500 ≥61
Drawn products Cold Drawing (K) + Spheroidizing Annealing (GKZ) + Finishing (K) ≤520 ≥61
1 Approximate Comparison Table
China Taiwan, China Japan South Korea Germany France Russia United Kingdom
GB ISC CNS JIS KS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
15CrH A20155 SCr415H SCr415H SCr415H 17Cr3 1.7016 17Cr3 15Х 17Cr3
(655M13)
2 Approximate Comparison Table structural alloy steel
China International Organization for Standardization Germany European Standard Russia United Kingdom
GB ISO DIN EN/DIN EN Numerical Grade GOST BS EN/BS
15CrH 17Cr3 17Cr3 17Cr3 1.7016 15KH 527M17
17Cr3 Corresponding Standards(Same grade name, different standards)
1 DIN 17210-1986
17Cr3 1.7016
2 EN 10084-1998
17Cr3 1.7016
3 EN 10263-3-2001
17Cr3 1.7016
4 DIN 1654-3-1989
17Cr 3 1.7016 (1.7015) (15Cr 3)
5 Q/BQB 517-2018
17Cr3
6 DIN EN 10263-3-2018
17Cr3 1.7016
7 EN 10263-3-2017
17Cr3 1.7016
8 DIN EN ISO 683-3-2019
17Cr3
9 ISO 683-3-2019
17Cr3
10 DIN EN 10084-2008
17Cr3 1.7016
11 ISO 4954-2018
17Cr3
12 EN 10132-2021
17Cr3 1.7016
13 NF EN 10084-2008
17Cr3 1.7016
14 ISO 4954-1-2024
17Cr3

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!