N06600 - ASTM B168-2019 - H2ABC

中文版

USA UNS	N06600
Corresponding Standard	ASTM B168-2019 Nickel-Chromium-Aluminum Alloys(UNS N06699) , Nickel-Chromium-Iron Alloys(UNS N06600,N06601,N06603,N06690,N06993,N06045,and N06696), Nickel-Chromium-Cobalt-Moly Alloy(UNS N06617), Nickel-Iron-Chromium-Tungsten Alloy(UNS N06674), and Nickel-Chromium-Molyb
Classification	Nickel and Nickel Alloys

Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	S	Cr	Ni	Cu
Minimum Value	6	-	-	-	-	14	72	-
Maximum Value	10	0.15	0.5	1	0.015	17	-	0.5

Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Plate,Sheet	Hot Rolled, Annealed	≥550	≥240	（in 50mm or 4D） ≥30
Plate	As-rolled	≥586	≥240	≥30
t＞0.25mm, Sheet/Strip	Cold Rolled, Annealed	≥550	≥240	≥30
t＞0.25mm, Sheet	Cold rolled, Hardened	≥860	≥620	≥2
Strip	Cold rolled, Skin-hard				HR B85~B88
Strip	Cold rolled, 1/4 hard,				HR B88~B94
Strip	Cold rolled, 1/2 hard,				HR B93~B98
Strip	Cold rolled, 3/4 hard				HR B97~C25
t＞0.25mm, Strip	Cold rolled, Hard	≥860	≥620	≥2
Strip	Cold rolled, Spring				HRC ≥30

Approximate Comparison Table Corrosion-Resistant Alloy

China		Japan	South Korea	United States		Germany		United Kingdom
GB	ISC	JIS	KS	Commercial Grade	UNS	W-Nr.	L-Nr.	BS EN/BS
NS 3102 (NS 312) (1Crl 5 Ni75Fe8)	H 06600 H 03102	NCF 600	NCF 600	Inconel 600	N 06600	NiCr15Fe	2.4816	NA 14