Grade 06Cr13Al
China ISC S11348
Old Grade
Corresponding Standard GB /T 1221-2007
Heat-resistant Steel Bars
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
06Cr13Al Chemical Element Composition Content (%)
Component C Si Mn P S Cr Al
Minimum Value - - - - - 11.5 0.1
Maximum Value 0.08 1 1 0.04 0.03 14.5 0.3
06Cr13Al Mechanical Properties
diameter
d
mm		 Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
d≤75 (annealed) ≥410 ≥175 ≥20 ≤183
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
06Cr13Al S11348 405 SUS 405 STS 405 405 S40500 X6CrAl 13 X6CrAl 13
(X7CrAl 13) 		1.4002 Z6CA 13 X6CrAl 13 1.4002 2302 405S17
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr13Al
(0Cr13Al) 		S11348 405 SUS 405 STR 405 405 S40500 X6CrAl 13
2
ISO 683-13-1986 		X6CrAl 13
(X7CrAl 13) 		1.4002 Z6CA 13 X6CrAl 13 1.4002 1Х20Ю 2302 405S17
06Cr13Al Corresponding Standards(Same grade name, different standards)
1 GB /T 20878-2007
06Cr13Al S11348 (0Cr13Al)
2 GB /T 1221-2007
06Cr13Al S11348 (0Cr13Al)
3 GB /T 1220-2007
06Cr13Al S11348 (0Cr13Al)
4 GB /T 4240-2019
06Cr13Al S11348
5 GB /T 3280-2015
06Cr13Al S11348 (0Cr13Al)
6 GB /T 4238-2015
06Cr13Al S11348 (0Cr13Al)
7 GB /T 4237-2015
06Cr13Al S11348 (0Cr13Al)
8 GB /T 14975-2012
06Cr13Al S11348 (0Cr13Al)
9 GB /T 12770-2012
06Cr13Al S11348 (0Cr13Al)
10 GB /T 14976-2012
06Cr13Al S11348 (0Cr13Al)
11 GB /T 12771-2019
06Cr13Al S11348
12 GB /T 24511-2017
06Cr13Al S11348
13 GB /T 20878-2024
06Cr13Al S11348 (0Cr13Al)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!